Назва: Influence of mechanochemical and ultrasonic treatments on the structure and properties of ZnO-MoO3 (1:1) composition
Автори: Sachuk, Olena
Kopachevska, Natalya
Zazhigalov, Valery
Starchevskyy, Volodymyr
Приналежність: Institute for sorption and problems of endoecology of NAS of Ukraine
Lviv Polytechnic National University
Бібліографічний опис: Influence of mechanochemical and ultrasonic treatments on the structure and properties of ZnO-MoO3 (1:1) composition / Olena Sachuk, Natalya Kopachevska, Valery Zazhigalov, Volodymyr Starchevskyy // Litteris et Artibus : proceedings of the 6th International youth science forum, November 24–26, 2016, Lviv, Ukraine / Lviv Polytechnic National University. – Lviv : Lviv Polytechnic Publishing House, 2016. – P. 430–431. – Bibliography: 2 titles.
Конференція/захід: Litteris et Artibus
Дата публікації: 2016
Видавництво: Lviv Polytechnic Publishing House
Країна (код): UA
Місце видання, проведення: Lviv
Теми: mechanochemistry
sonochemistry
zinc oxide
molybdenum oxide
zinc molybdates
Кількість сторінок: 430-431
Короткий огляд (реферат): Oxide mixture ZnO-MoO3 (1:1) was modified by mechanochemical (during 2, 4 and 8 hours in air) and sonochemical (1 hr in water solution) treatments. The properties of obtained samples were studied by means of XRD, IR-spectroscopy, BET, DTA-TG, SEM methods. It was shown, that both kinds of treatments lead to the change of oxides crystalline structure, their surface morphology, porous structure and decrease particle size. The formation β-ZnMoO4 in the milling process and β-Мо8О23 at ultrasonic effect it was found.
URI (Уніфікований ідентифікатор ресурсу): http://ena.lp.edu.ua:8080/handle/ntb/41043
References: [1] K.T.Queeney, C.M.Friend, "Site-selective surface reactions: Hydrocarbon oxidation processes on oxidized Mo (110)," J. Phys. Chem., vol. 104, pp.409-415. [2] Y.W. Wang, L.D. Zhang, G.Z. Wang, et al., "Catalytic growth of semiconducting zinc oxide nanowires and their photoluminescence properties," Journal of Crystal Growth, vol. 234, pp.171-175.
Тип вмісту : Conference Abstract
Розташовується у зібраннях:Litteris et Artibus. – 2016 р.

Файли цього матеріалу:
Файл Опис РозмірФормат 
LEA-2016-430-431.pdf523,88 kBAdobe PDFПереглянути/відкрити


Усі матеріали в архіві електронних ресурсів захищені авторським правом, всі права збережені.