Назва: Tribotechnical characteristics of VT22 titanium alloy after nitriding, combined with heat treatment
Автори: Lavrys, Serhii
Kovbasyuk, Taras
Penkovyi, Oleh
Приналежність: Karpenko Physico-Mechanical Institute of the NAS of Ukraine
Lviv Polytechnic National University
Бібліографічний опис: Lavrys S. Tribotechnical characteristics of VT22 titanium alloy after nitriding, combined with heat treatment / Serhii Lavrys, Taras Kovbasyuk, Oleh Penkovyi // Litteris et Artibus : proceedings of the 6th International youth science forum, November 24–26, 2016, Lviv, Ukraine / Lviv Polytechnic National University. – Lviv : Lviv Polytechnic Publishing House, 2016. – P. 302–303. – Bibliography: 2 titles.
Конференція/захід: Litteris et Artibus
Дата публікації: 2016
Видавництво: Lviv Polytechnic Publishing House
Країна (код): UA
Місце видання, проведення: Lviv
Теми: VT22 titanium alloy
heat treatment
nitriding
surface hardening and tribotechnical characteristics
Кількість сторінок: 302-303
Короткий огляд (реферат): Nitriding of VT22 titanium alloy, combined with its standard heat treatment in a single technological cycle was proposed. It was shown that after thermodiffusion saturation the microhardness and depth of the hardened surface layer of VT22 alloy increased, but the quality machined surface worsened. It was established that the increase time of nitriding process worsened the tribotechnical characteristics of friction pair nitrided VT22 alloy – BrAZhN 10-4-4 bronze.
URI (Уніфікований ідентифікатор ресурсу): http://ena.lp.edu.ua:8080/handle/ntb/40882
References: [1] Inagaki I., Takechi T., Shirai Y., Ariyasu N. “Appli-cation and Features of Titanium for the Aerospace Industry”, Nippon Steel & Sumitomo Metal Technical Report, Vol. 106, pp. 22–82, July. 2014. [2] Yan M. F., Zhu Y. D., Zhang Y. X., Zhang M. L., “Combining thermo-diffusing titanium and plasma nitriding to modify C61900 Cu–Al alloy”, Vacuum, Vol. 126, pp. 41–44, April. 2016.
Тип вмісту : Conference Abstract
Розташовується у зібраннях:Litteris et Artibus. – 2016 р.

Файли цього матеріалу:
Файл Опис РозмірФормат 
LEA-2016-302-303.pdf573,87 kBAdobe PDFПереглянути/відкрити


Усі матеріали в архіві електронних ресурсів захищені авторським правом, всі права збережені.